Teknoloji avanse tretman chalè pou fè manifakti | Shangdong Yueheng

Tretman chalè gouvène pote mesures pèfòmans ki gen ladan kontak lavi fatig (L10 Rating), rezistans mete, ak estabilite dimansyon. Pwodiksyon modèn mande pou ± 3 ° C kontwòl tanperati ak Pwosesis kapasite CPK≥1.33. Sekans Nwayo: Spheroidizing rkwir → quenching → tanperati ki ba-tanperati → estabilizasyon.

1.Sheroidizing rkwir

Objektif: Elimine tou, rezo carbure (≤grade 2), fòme omojèn pyèj spheroidized (carbure spheroidization ≥90%, dyamèt 0.2-0.6μm), dite 179-207 Hb. Pwotokòl de etap:

• Etap 1: 790 ± 10 ° C × 2-4H austenitization (pasyèl carbure yap divòse)
• Etap 2: 710 ± 10 ° C × 4-6H refwadisman dousman (≤20 ° C/h) a 650 ° C, Kontwole koub refwadismanAnpeche presipitasyon carbure koryas

Paramèt kritik: Gwosè grenn 7-8 (ASTM E112)

2. Pwosesis

Sèl Bath (BACL₂: KCl = 3: 1) oswa atmosfè pwoteksyon (N₂-ch₃OH, sond oksijèn ≤0.5%):

• GCR15 Steel: 845 ± 5 ° C × faktè tan (epesè miray × 0.8-1.2 min/mm)
• Cinétique refwadisman: 800 → 500 ° C pousantaj refwadisman ≥45 ° C/s (evite fòmasyon ferit), ralanti refwadisman anba a 300 ° C
• Sib: cryptocrystalline martensit (> 95%, zegwi longè ≤0.02mm) + double klas austenit (<5%)

3.Low-tanperati tanperaman

150-180 ° C × 2-4H (± 3 ° C) nan fòse konveksyon lè gwo founo dife:

• ε-Fe₂.₄c presipitasyon nan martensit, dite 61-65 HRC
• Austenit dekonpozisyon:> 80% (XRD verifye)
• Estrès modèl sekou: σ_residual = σ_initial × E^(-0.02t) (t nan èdtan)

4. Pwosesis Espesyal ak Innovations

• Austempering: 230 ± 10 ° C beny sèl × 2H → Lower Bainite (58-62 HRC, KCV≥50J/cm ²)
• Gwo twou san fon cro: -70 ° C × 4H (espre nitwojèn likid), austenit → transfòmasyon martensit> 95%
• Lazè redi: 1064nm longèdonn kreye 0.3mm ka pwofondè, ↑ 40% kontak fatig lavi

Kadri Kalite Asirans: